Unveiling the effect of Ti substitutions on the static oxidation behavior of (Hf,Ti)C at 2500 ℃

Hf-based carbides are highly desirable candidates for thermal protection applications above 2000 ℃ due to their extremely high melting point and favorable mechanical properties. However, as a crucial indicator for composition design and performance assessment, the static oxidation behavior of Hf-based carbides at their potential service temperatures has been rarely studied.

In a study published in the KeAi journal Advanced Powder Materials, a group of researchers from Central South University and China Academy of Launch Vehicle Technology revealed the static oxidation mechanism of (Hf, Ti)C bulks at 2500 ℃, as well as the effect of Ti substitutions on their oxidation behaviors.

“The addition of Ti element can make the microstructure of HfC oxide layer more complex,” explained Shiyan Chen, lead author of the study. “Typically, such a composite oxide layer has better protective properties.”

The thickness of the oxide layer on the surface of (Hf, Ti)C was reduced by 62.29 % compared with that on the HfC monocarbide surface after oxidation at 2500 ℃ for 2000 s. The dramatic improvement in oxidation resistance was attributed to the unique oxide layer structure consisting of various crystalline oxycarbides, HfO₂ and carbon.

“The Ti-rich oxycarbide ((Ti, Hf)C_xO_y) dispersed within HfO₂ formed the major structure of the oxide layer. A coherent boundary with lattice distortion existed at the HfO₂ / (Ti, Hf)C_xO_y interface along the (111) crystal plane direction, which served as an effective oxygen diffusion barrier,” added Chen.

The Hf-rich oxycarbide ((Hf, Ti)C_xO_y) together with (Ti, Hf)C_xO_y, HfO₂, and precipitated carbon constituted a dense transition layer, ensuring favorable bonding between the oxide layer and the matrix. Furthermore, the Ti content affects the diffusion of carbon in (Hf, Ti)C lattice and the distribution of Ti-rich oxycarbide, which will further determine the structural integrity of the oxide layer. Based on the results of oxidation kinetics, 30%-40 at. % Ti substitution provides the best enhancement of oxidation resistance.

According to Professor Zhaoke Chen, co-lead and corresponding author, this study represents a novel exploration in the field of ultra-high temperature ceramics (UHTCs). “Our study enhances the comprehension of the structural evolution during ultra-high temperature oxidation. The findings offer theoretical guidance for optimizing the composition of UHTCs to broaden their applications at ultra-high temperatures,” said Chen.

###

References

DOI

10.1016/j.apmate.2023.100168

Original Source URL

https://doi.org/10.1016/j.apmate.2023.100168

Funding information

This work was supported by the National Natural Science Foundation of China grant numbers [52072410].

Journal

Advanced Powder Materials